Black Neoprene Anti Static BS490 & Flame Retardant ISO 340 Sheet 60° shore 1mm – 10mm

ATEX Compliant
Working Voltage: ISO340
Compliant to: BS490
  • Flame Resistant According to ISO 340
  • Anti-Static Characteristics According to BS490
  • REACH, RoHS, PAH and CE compliant
  • High Grade Flame Retardant Neoprene: 60° Shore
  • ATEX Compliant
Product total
Options total
Grand total
EM187 – Black Anti Static (British Standard BS490 with 3 x 108 surface electrical resistance Ω maximum) and Flame Retardant to ISO 340 standard 60° shore. N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Material Profile (see below):
  • Thickness: 1mm, 1.5mm, 2mm, 2.5mm, 3mm, 4mm, 5mm, 6mm, 8mm, 10mm
  • Sheet Size: 1.4m wide in 10m rolls
  • Cutting: Standard press tools
Flame resistance (according to ISO 340)

– Flame persistence (after removing the burner)

– Flame persistence must be under 45 sec

– For each six groups of test pieces and each single value under 15 sec

– The flame mustn’t reappear after an air draft application

Antistatic characteristic (according to BS 490)

– Surface electrical resistance ( ), max Other grades, colours and finishes are available – subject to minimum batch quantities.

Characteristics

Values

Specific Gravity

1.20

Hardness (o Shore A)

60 ± 5

Tensile Strength, (Kgf/cm2), min

80

Elongation At Break, (%), min

250

Maximum compression set after 24h at 70oC, (%)

25

Flame resistance (according to ISO 340)

Flame persistence (after removing the burner)

Max 45s

The flame mustn’t reappear after an air draughtiness application

Max 15

Antistatic characteristic (according to BS 490)

Surface electrical resistance (Ω), max

3 x 108

Temperature Range

-30o to +100oC

Compression Set (70oC for 22 hours), (%)

25

Polymer Content

Blend